製品詳細
支払いと送料の条件
Structure: |
Alien |
Compressive Strength: |
2200Mpa |
After Warranty Service: |
Online support |
Transparency: |
Opaque |
Chemical Resistance: |
High |
Vickers Hardulus: |
1150 HV1/2 |
Tooth Form: |
flat tooth |
Elastic Modulus: |
210Gpa |
Use: |
textile industry |
Speed: |
General Speed Mechanical Seal |
Impact Resistance: |
12 MPam1/2 |
Dielectric Constant: |
9.5 |
Material: |
Zirconia |
Bending Strength: |
950-1200 Mpa |
Printing Type: |
Pad printing machine |
Structure: |
Alien |
Compressive Strength: |
2200Mpa |
After Warranty Service: |
Online support |
Transparency: |
Opaque |
Chemical Resistance: |
High |
Vickers Hardulus: |
1150 HV1/2 |
Tooth Form: |
flat tooth |
Elastic Modulus: |
210Gpa |
Use: |
textile industry |
Speed: |
General Speed Mechanical Seal |
Impact Resistance: |
12 MPam1/2 |
Dielectric Constant: |
9.5 |
Material: |
Zirconia |
Bending Strength: |
950-1200 Mpa |
Printing Type: |
Pad printing machine |
ジルコニア（ZrO₂）精密セラミックスは、その卓越した特性の組み合わせにより、最先端材料として台頭してきました。優れた機械的強度（曲げ強度 ≥1000MPa）、驚異的な破壊靭性（8-10 MPa·m¹/²）、および優れた生体適合性（ISO 13356認証）を備え、この材料は医療、電子機器、産業用途において比類のない性能を発揮します。
生医学分野では、ジルコニアセラミック歯科修復物は、自然な美しさ（45～50％の光透過率）と10年を超える臨床的な長寿命を両立しています。家電製品では、その優れた誘電特性（ε=28-32）と耐衝撃性により、5G対応デバイスに最適です。産業用途では、過酷な動作条件下でも信頼性の高い性能を維持するジルコニア精密ベアリングが活用されています。
当社は、材料開発から最終製品まで、ホットイソスタティックプレスや精密研磨などの高度なプロセスを活用し、カスタマイズされた高性能コンポーネントを提供し、エンドツーエンドのソリューションを提供しています。ジルコニア精密セラミックスを選択することは、強度、美しさ、信頼性を完璧にバランスさせた、将来性のある材料を選択することです。